Nanocrystalline LiCrTiO4 as anode for asymmetric hybrid supercapacitor

---

Abstract.
Lithiated spinel, LiCrTiO4 is synthesized by sonochemical method followed by calcination at 923 K for 2 h.
The prepared material is characterized by powder X-ray diffraction (XRD), scanning electron microscopy
(SEM), transmission electron microscopy (TEM) and energy dispersion X-ray spectroscopy (EDX). Cubic
phase LiCrTiO4 with Fd3m space group is evident from the XRD. Particles of 60–70 nm in size are observed
from the microscopic images. The presence of respective elements is confirmed from EDX analysis. The
electrochemical characteristics of LiCrTiO4 electrode were evaluated in a lithium battery cell. It has been
found that the intercalation of lithium ions into LiCrTiO4 lattice occurs at 1.5 and 1.65 V vs. Li/Li+ with ionic conduction behavior. A reversible specific capacity of ∼160 mAh/g was obtained. Nanocrystalline LiCrTiO4 is exploited as anode for asymmetric hybrid supercapacitor and the electrochemical performance is
investigated. The cell exhibited a specific capacity of 59 mAh/g at 1 mA/cm2 in a non-aqueous electrolyte.
It also showed good cycling performance for 1000 cycles with 96% retention in capacity.

Keywords: Nanocrystalline LiCrTiO4, Anode, Asymmetric hybrid supercapacitor, Sonochemical method

---

Ketersediaan

Tidak ada salinan data

Informasi Detail

Judul Seri

Solid State Ionics

No. Panggil

-

Penerbit

New York : Elsevier B.V.., 2010

Deskripsi Fisik

Solid State Ionics 181 (2010) 839–843

Bahasa

English

ISBN/ISSN

-

Klasifikasi

-

Tipe Isi

-

Tipe Media

-

Tipe Pembawa

-

Edisi

-

Subjek

FISIKA MATERIAL

Info Detail Spesifik

-

Pernyataan Tanggungjawab

agus

Versi lain/terkait

Lampiran Berkas

Komentar

---

Anda harus masuk sebelum memberikan komentar