Preparation and characterisation of epitaxial Pt/Cu/FeMn/Co thin films on (100)-oriented MgO single crystals

---

FeMn/Co thin-films, a purely metallic exchange-bias system,were prepared on (100)-oriented MgO single crystals. The
layers were grown by molecular beam epitaxy (MBE). The crystalline and magnetic properties could be tuned by using
sputtered Pt buffer layers deposited at variable temperatures. A transition of the crystalline orientation from (111)-terminated layers at lower deposition temperatures to (100)-terminated layers at temperatures higher than 950K was established and the impact on the magnetic sample properties was investigated. Here, the detailed sample preparation process is shown together with low energy electron diffraction (LEED),medium energy electron diffraction (MEED), atomic force microscopy (AFM), X-ray photoelectron spectroscopy (XPS),X-ray diffraction (XRD) and transmission electron microscopy (TEM) measurements revealing the samples structure and composition. The crystalline orientation of Pt was imprinted to the magnetic layer stack and clearly influenced the exchangebias (EB) and coercive field (HC) as shown by superconducting quantum interference device (SQUID) and magneto-optical Kerr effect (MOKE) measurements. Furthermore, a correlation between the crystallite size and the temperature dependent magnetic properties could be identified.

Keywords exchange-bias, FeMn/Co, magnetism, molecular beam epitaxy

---

Ketersediaan

Tidak ada salinan data

Informasi Detail

Judul Seri

Phys. Status Solidi

No. Panggil

-

Penerbit

: WILEY-VCH Verlag GmbH & Co. KGaA., 2015

Deskripsi Fisik

Phys. Status Solidi A 212, No. 10, 2114–2123 (2015)

Bahasa

English

ISBN/ISSN

-

Klasifikasi

-

Tipe Isi

-

Tipe Media

-

Tipe Pembawa

-

Edisi

-

Subjek

FISIKA

Info Detail Spesifik

-

Pernyataan Tanggungjawab

Wati/Agus

Versi lain/terkait

Lampiran Berkas

Komentar

---

Anda harus masuk sebelum memberikan komentar